- 熔體流動(dòng)速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.77
- 拉伸強(qiáng)度 [MPa]: 57.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 - 1.79 g/cc | 0.0639 - 0.0647 lb/in3 | ASTM D792 |
| Viscosity | 2200 cP @Shear Rate 50.0 1/s, Temperature 240 °C | 2200 cP @Shear Rate 50.0 1/s, Temperature 464 °F | Melt; ASTM D3835 |
| Viscosity Test | 1.0 cm3/g @Temperature 30.0 °C | 1.0 cm3/g @Temperature 86.0 °F | Inherent Viscosity in DMF Solution |
| Melt Flow | 6.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 6.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | ISO 527-2 |
| Elongation at Break | 28 % | 28 % | ISO 527-2 |
| Tensile Modulus | 2.33 GPa | 338 ksi | ISO 527-2 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1e+15 - 1e+16 ohm-cm | 1e+15 - 1e+16 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 173 °C | 343 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | ISO 75-2 |
| Flammability, UL94 | V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | |
- 關(guān)鍵詞:
- pvdf
- 供應(yīng)
- Kureha KF Polymer 1000 PVDF Homopolymer