- 密度 [g/cm3]: 1.77
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 1.6
- 彎曲模量 [MPa]: 2.14
- 硬度: 100.0
- 熱變形溫度 [℃]: 149.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.78 g/cc | 1.78 g/cc | ASTM D792 |
| Density | 1.77 g/cc | 0.0640 lb/in3 | ASTM D792 |
| Water Absorption | 0.020 % @Temperature 22.8 °C, Time 86400 sec | 0.020 % @Temperature 73.0 °F, Time 24.0 hour | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength at Break | 53.8 MPa @Temperature 22.8 °C | 7800 psi @Temperature 73.0 °F | ASTM D638 |
| Elongation at Break | 35 % @Temperature 22.8 °C | 35 % @Temperature 73.0 °F | ASTM D638 |
| Tensile Modulus | 2.41 GPa @Temperature 22.8 °C | 350 ksi @Temperature 73.0 °F | ASTM D638 |
| Flexural Strength | 74.12 MPa @Temperature 22.8 °C | 10750 psi @Temperature 73.0 °F | ASTM D790 |
| Flexural Modulus | 2.14 GPa @Temperature 22.8 °C | 310 ksi @Temperature 73.0 °F | ASTM D790 |
| Compressive Strength | 80.0 MPa @Temperature 22.8 °C | 11600 psi @Temperature 73.0 °F | ASTM D695 |
| Izod Impact, Notched | 1.60 J/cm @Temperature 22.8 °C | 3.00 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 5.00e+14 ohm-cm @Temperature 22.8 °C | 5.00e+14 ohm-cm @Temperature 73.0 °F | ASTM D257 |
| Dielectric Constant | 9.0 @Frequency 60.0 Hz, Temperature 22.8 °C | 9.0 @Frequency 60.0 Hz, Temperature 73.0 °F | 50% RH; ASTM D150 |
| Dielectric Strength | 11.0 kV/mm | 280 kV/in | ASTM D149 |
| Dissipation Factor | 0.060 @Frequency 60.0 Hz, Temperature 22.8 °C | 0.060 @Frequency 60.0 Hz, Temperature 73.0 °F | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 128 μm/m-°C | 71.0 μin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft2-°F | ASTM C177 |
| Melting Point | 172 °C | 342 °F | ASTM D3448 |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |