- 熔體流動速率 [g/10min]: 3.0
- 吸水率 [%]: 0.03
- 缺口沖擊強度: 5.34
- 拉伸強度 [MPa]: 20.0
- 彎曲模量 [MPa]: 0.620
- 熱變形溫度 [℃]: 60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.76 - 1.80 g/cc | 1.76 - 1.80 g/cc | ASTM D792 |
| Bulk Density | 0.961 g/cc | 0.0347 lb/in3 | |
| Water Absorption | 0.030 - 0.050 % @Time 86400 sec | 0.030 - 0.050 % @Time 24.0 hour | Immersion; ASTM D570 |
| Viscosity | 2.20e+6 - 2.70e+6 cP @Shear Rate 100 1/s, Temperature 232 °C | 2.20e+6 - 2.70e+6 cP @Shear Rate 100 1/s, Temperature 450 °F | Melt Viscosity; ASTM D3835 |
| Melt Flow | 3.0 - 8.0 g/10 min @Load 12.5 kg, Temperature 232 °C | 3.0 - 8.0 g/10 min @Load 27.6 lb, Temperature 450 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 - 70 | 65 - 70 | ASTM D2240 |
| Tensile Strength at Break | 17.0 - 34.0 MPa | 2470 - 4930 psi | ASTM D638 |
| Tensile Strength, Yield | 20.0 - 34.0 MPa | 2900 - 4930 psi | ASTM D638 |
| Elongation at Break | 200 - 400 % | 200 - 400 % | ASTM D638 |
| Elongation at Yield | 10 - 20 % | 10 - 20 % | ASTM D638 |
| Tensile Modulus | 0.551 - 0.896 GPa | 79.9 - 130 ksi | ASTM D638 |
| Flexural Strength | 20.0 - 34.0 MPa @Strain 5.00 % | 2900 - 4930 psi @Strain 5.00 % | ASTM D790 |
| Flexural Modulus | 0.620 - 0.827 GPa | 89.9 - 120 ksi | ASTM D790 |
| Compressive Strength | 31.0 - 41.0 MPa | 4500 - 5950 psi | ASTM D695 |
| Izod Impact, Notched | 5.34 - 10.7 J/cm | 10.0 - 20.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | >= NB | >= NB | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.33 | 0.33 | vs. steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.33 | 0.33 | vs. steel; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 16 - 19 | 16 - 19 | 1000 g pad; CS-17 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+14 ohm-cm @Temperature 20.0 °C | 2.00e+14 ohm-cm @Temperature 68.0 °F | 65% RH; ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1.00e+8 Hz | 3.5 @Frequency 1.00e+8 Hz | ASTM D150 |
| 10.6 @Frequency 100 Hz | 10.6 @Frequency 100 Hz | ASTM D150 | |
| Dielectric Strength | 51.2 - 59.1 kV/mm | 1300 - 1500 kV/in | ASTM D149 |
| Dissipation Factor | 0.020 - 0.21 @Frequency 100 Hz | 0.020 - 0.21 @Frequency 100 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 126 - 185 μm/m-°C | 70.0 - 103 μin/in-°F | ASTM D696 |
| Specific Heat Capacity | 1.17 - 1.51 J/g-°C | 0.280 - 0.360 BTU/lb-°F | DSC |
| Thermal Conductivity | 0.144 - 0.180 W/m-K | 1.00 - 1.25 BTU-in/hr-ft2-°F | ASTM D433 |
| Melting Point | 140 - 145 °C | 284 - 293 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 75.0 °C | 140 - 167 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 - 55.0 °C | 104 - 131 °F | ASTM D648 |
| Glass Transition Temp, Tg | -41.0 - -39.0 °C @Frequency 1.00 Hz | -41.8 - -38.2 °F @Frequency 1.00 Hz | DMA |
| Decomposition Temperature | 375 °C | 707 °F | 1% wt loss / in air; TGA |
| 410 °C | 770 °F | 1% wt loss / in nitrogen; TGA | |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 42 % | 42 % | ASTM D2868 |
| 75 % | 75 % | optional products; ASTM D2868 | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 195 - 220 °C | 383 - 428 °F | Tube Extrusion |
| Middle Barrel Temperature | 210 - 240 °C | 410 - 464 °F | Tube Extrusion |
| Front Barrel Temperature | 210 - 240 °C | 410 - 464 °F | Tube Extrusion |
| Die Temperature | 210 - 250 °C | 410 - 482 °F | Tube Extrusion |
| Head Temperature | 210 - 240 °C | 410 - 464 °F | Tube Extrusion |