- 熔體流動速率 [g/10min]: 2.6
- 密度 [g/cm3]: 1.78
- 吸水率 [%]: 0.02
- 拉伸強度 [MPa]: 50.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in3 | |
| Water Absorption | 0.020 % | 0.020 % | |
| Moisture Absorption at Equilibrium | 0.015 % | 0.015 % | Humidity Absorption |
| Melt Flow | 2.6 g/10 min @Load 5.00 kg, Temperature 230 °C | 2.6 g/10 min @Load 11.0 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min |
| Elongation at Break | 8.0 % | 8.0 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10000 ohm-cm | 10000 ohm-cm | |
| Surface Resistance | 10000 ohm | 10000 ohm | |
| Dissipation Factor | 0.071 @Frequency 100 Hz | 0.071 @Frequency 100 Hz | |
| 0.37 @Frequency 1e+6 Hz | 0.37 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 171 °C | 340 °F | 10°C/min |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | |
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | 10°C/min |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | ||