- 熔體流動(dòng)速率 [g/10min]: 7.0
- 拉伸強(qiáng)度 [MPa]: 6.0
- 彎曲強(qiáng)度 [MPa]: 38.0
- 彎曲模量 [MPa]: 0.645
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.75 - 1.79 g/cc | 1.75 - 1.79 g/cc | ASTM D792 | ||
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D3159 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D1708 | ||
| 3.50 MPa @Temperature 200 °C | 508 psi @Temperature 392 °F | ASTM D1708 | |||
| Tensile Strength, Yield | 6.00 MPa @Temperature 180 °C | 870 psi @Temperature 356 °F | ASTM D1708 | ||
| Elongation at Break | 300 % | 300 % | ASTM D1708 | ||
| 600 % @Temperature 180 °C | 600 % @Temperature 356 °F | ASTM D1708 | |||
| Flexural Modulus | 0.645 GPa | 93.6 ksi | ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 245 - 250 °C | 473 - 482 °F | ASTM D3159 | ||
| Oxygen Index | >= 34 % | >= 34 % | |||
| Descriptive Properties | |||||
| Folding Endurance, # cycles, .18-.20 mm | 120000 | ||||