- 熔體流動(dòng)速率 [g/10min]: 7.0
- 拉伸強(qiáng)度 [MPa]: 6.205
- 彎曲強(qiáng)度 [MPa]: 37.92
- 彎曲模量 [MPa]: 1.172
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.75 - 1.79 g/cc | 1.75 - 1.79 g/cc | ASTM D792 | ||
| Water Absorption | <= 0.030 % | <= 0.030 % | 24 hours; ASTM D570 | ||
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D3159 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 72 | 72 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 37.92 MPa | 5500 psi | ASTM D1708 | ||
| 3.447 MPa @Temperature 200 °C | 500.0 psi @Temperature 392 °F | ASTM D1708 | |||
| Tensile Strength, Yield | 6.205 MPa @Temperature 180 °C | 900.0 psi @Temperature 356 °F | ASTM D1708 | ||
| Elongation at Break | 300 % | 300 % | ASTM D1708 | ||
| 600 % @Temperature 180 °C | 600 % @Temperature 356 °F | ASTM D1708 | |||
| Flexural Modulus | 1.172 GPa | 170.0 ksi | ASTM D790 | ||
| Izod Impact, Notched | NB | NB | ASTM D256 | ||
| Coefficient of Friction | 0.30 - 0.40 | 0.30 - 0.40 | ASTM D1894 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | ASTM D257 | ||
| Surface Resistivity per Square | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D257 | ||
| Dielectric Constant | 2.6 @Frequency 1e+6 Hz | 2.6 @Frequency 1e+6 Hz | ASTM D150 | ||
| Dielectric Strength | 79.0 kV/mm | 2010 kV/in | 100 micrometers film; ASTM D149 | ||
| Dissipation Factor | 0.0070 @Frequency 1e+6 Hz | 0.0070 @Frequency 1e+6 Hz | ASTM D150 | ||
| Arc Resistance | 122 sec | 122 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 - 255 °C | 428 - 491 °F | ASTM D3159 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | 30 - 36 % | 30 - 36 % | Limiting Oxygen Index; ASTM D2863 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 302 - 323 °C | 576 - 613 °F | Cure Temperature | ||
| Descriptive Properties | |||||
| 20% Hydrochloric Acid Transmission, g/100sq in. | <0.02 | ||||
| 50% Sodium Hydroxide Transmission, g/100sq in. | <.02 | ||||
| Acetic Acid Transmission, g/100sq in. | 0.41 | ||||
| Acetone Transmission, g/100sq in. | 0.95 | ||||
| Acetophenone Transmission, g/100sq in. | 0.5 | ||||
| Benzene Transmission, g/100sq in. | 0.64 | ||||
| Carbon Tetrachloride Transmission, g/100sq in. | 0.31 | ||||
| Chemical/Solvent Resistance | Excellent | ||||
| Ethyl Acetate Transmission, g/100sq in. | 0.76 | ||||
| Folding Endurance, # cycles, .18-.20 mm | 120000 | ||||
| Heat of Combustion J/g | 13700 | ASTM D240 | |||
| Hexane Transmission, g/100sq in. | 0.56 | ||||
| Piperidine Transmission, g/100sq in. | 0.04 | ||||
| Red Fuming Nitric Acid Transmission, g/100sq in. | 7.5-1.4 | ||||
| Salt Spray Resistance on aluminum, Hours | 1000 | ||||
| Sulfuric Acid Transmission, g/100sq in. | 0.00001 | ||||
| Water Transmission, g/100sq in. | 0.4 | ||||
| Weather Resistance | 15 | Years unaffected in Florida Exposure | |||