- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.938
- 拉伸強度 [MPa]: 18.0
- 彎曲模量 [MPa]: 0.650
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | ISO 1872/1 |
| Environmental Stress Crack Resistance | 200 hour | 200 hour | F50; BP 13C/25 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg | 4.0 g/10 min @Load 4.76 lb | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | BP 13B/1 |
| Elongation at Break | 1400 % | 1400 % | BP 13B/1 |
| Flexural Modulus | 0.650 GPa | 94.3 ksi | ISO 178-1975 |
| Charpy Impact, Notched | 2.00 J/cm2 | 9.52 ft-lb/in2 | ISO 179 |