- 熔體流動速率 [g/10min]: 0.26
- 密度 [g/cm3]: 0.938
- 吸水率 [%]: 0.01
- 拉伸強度 [MPa]: 20.0
- 熱變形溫度 [℃]: 69.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | |
| Water Absorption | 0.010 % | 0.010 % | |
| Melt Flow | 0.26 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.26 g/10 min @Load 4.76 lb, Temperature 374 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 8.0 % | 8.0 % | |
| Tensile Modulus | 0.700 GPa | 102 ksi | |
| Tensile Impact Strength | 200 kJ/m2 | 95.2 ft-lb/in2 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 128 °C | 262 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 41.0 °C | 106 °F | |
| Vicat Softening Point | 65.0 °C | 149 °F | |
| Flammability, UL94 | HB @Thickness 0.400 mm | HB @Thickness 0.0157 in | |