- 熔體流動速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.938
- 彎曲強度 [MPa]: 20.6
- 彎曲模量 [MPa]: 0.860
- 熱變形溫度 [℃]: 49.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | ASTM D792 |
| ESCR 100% Igepal? | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | F50; Condition A, From compression molded specimens; ASTM D1693 |
| ESCR 10% Igepal? | 110 hour @Temperature 50.0 °C | 110 hour @Temperature 122 °F | F50; Condition A, From compression molded specimens; ASTM D1693 |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 20.6 MPa @Thickness 3.17 mm | 2990 psi @Thickness 0.125 in | Type IV specimen, 2" per minute test speed, rotomolded samples; ASTM D638 |
| Flexural Modulus | 0.860 GPa | 125 ksi | 1% Strain Value from rotomolded samples; ASTM D790 |
| Impact Test | 70.0 J @Thickness 3.17 mm, Temperature -40.0 °C | 51.6 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | rotomolded; ARM Method |
| 220 J @Thickness 6.35 mm, Temperature -40.0 °C | 162 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | rotomolded; ARM Method | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 38.0 °C | 100 °F | ASTM D648 |