- 熔體流動(dòng)速率 [g/10min]: 4.2
- 密度 [g/cm3]: 0.935
- 缺口沖擊強(qiáng)度: 1.44
- 拉伸強(qiáng)度 [MPa]: 14.0
- 斷裂伸長(zhǎng)率 [%]: 15.0
- 彎曲模量 [MPa]: 0.480
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in3 | ASTM D1505 |
| Melt Flow | 4.2 g/10 min @Load 2.16 kg | 4.2 g/10 min @Load 4.76 lb | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
| Elongation at Break | 930 % | 930 % | ASTM D638 |
| Flexural Yield Strength | 15.0 MPa | 2180 psi | ASTM D790 |
| Flexural Modulus | 0.480 GPa | 69.6 ksi | ASTM D790 |
| Izod Impact, Notched | 1.44 J/cm | 2.70 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 116 °C | 241 °F | ASTM D1525 |