- 熔體流動速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.938
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | ASTM D792 |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 15.0 MPa | 2180 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 16.0 MPa | 2320 psi | ASTM D882 |
| Film Elongation at Break, MD | 800 % | 800 % | ASTM D882 |
| Film Elongation at Break, TD | 1070 % | 1070 % | ASTM D882 |
| Secant Modulus, MD | 0.320 GPa | 46.4 ksi | at 1%; ASTM D882 |
| Secant Modulus, TD | 0.380 GPa | 55.1 ksi | at 1%; ASTM D882 |
| Impact | 80 | 80 | J/mm; NOVA Chemicals Puncture test |
| Coefficient of Friction | >= 0.80 | >= 0.80 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 1.40 g/micron | 35.6 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 8.00 g/micron | 203 g/mil | ASTM D1922 |
| Film Tensile Strength at Break, MD | 41.0 MPa | 5950 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 87 % | 87 % | at 45°; ASTM D2457 |