- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.94
- 彎曲模量 [MPa]: 0.690
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in3 | ASTM D1505 | ||
| Melt Flow | 0.20 g/10 min | 0.20 g/10 min | I2; ASTM D1238 | ||
| 20 g/10 min | 20 g/10 min | I21; ASTM D238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 | ||
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 | ||
| Flexural Modulus | 0.690 GPa | 100 ksi | at 1% elongation; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 125 °C | 257 °F | Petromont | ||
| Vicat Softening Point | 116 °C | 241 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Process | Film | ||||