- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.935
- 拉伸強度 [MPa]: 18.6
- 彎曲模量 [MPa]: 0.689
- 熱變形溫度 [℃]: 60.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in3 | ASTM D1505 | ||
| ESCR 100% Igepal? | >= 1000 hour | >= 1000 hour | ASTM D1693 | ||
| ESCR 10% Igepal? | >= 200 hour | >= 200 hour | ASTM D1693 | ||
| Melt Flow | 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.00 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | 2 in/min; ASTM D638 | ||
| Tensile Strength, Yield | 18.6 MPa | 2700 psi | 2 in/min; ASTM D638 | ||
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 | ||
| Elongation at Yield | 12.0 % | 12.0 % | ASTM D638 | ||
| Flexural Modulus | 0.689 GPa | 100 ksi | 1% Secant; ASTM D790 | ||
| Impact Test | 67.8 J @Temperature -40.0 °C | 50.0 ft-lb @Temperature -40.0 °F | 0.125 in.; ARM STD test | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Process | Rotational Molding | ||||
| Region | Europe/Turkey | ||||