- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.938
- 拉伸強度 [MPa]: 15.0
- 彎曲模量 [MPa]: 0.650
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | ASTM 1505-68 |
| Environmental Stress Crack Resistance | 400 hour | 400 hour | ASTM D1693 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238-7 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ASTM D638-72 |
| Elongation at Break | >= 900 % | >= 900 % | ASTM D638 |
| Flexural Modulus | 0.650 GPa | 94.3 ksi | ASTM D790 |
| Charpy Impact, Notched | 1.80 J/cm2 | 8.57 ft-lb/in2 | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.480 W/m-K | 3.33 BTU-in/hr-ft2-°F | ASTM D177 |
| Vicat Softening Point | 115 °C | 239 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 131 °C | 268 °F | |