- 熔體流動速率 [g/10min]: 0.1
- 密度 [g/cm3]: 0.955
- 拉伸強度 [MPa]: 24.0
- 彎曲模量 [MPa]: 1.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in3 | ISO 1183 | ||
| Viscosity | 1.60e+6 cP @Shear Rate 100 1/s, Temperature 190 °C | 1.60e+6 cP @Shear Rate 100 1/s, Temperature 374 °F | ATOFINA research test | ||
| Environmental Stress Crack Resistance | >= 700 hour | >= 700 hour | ASTM D1693 | ||
| Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 | ||
| >= 30 min | >= 30 min | 200°C; EN 728 | |||
| Carbon Black Loading | 2.0 - 2.5 % | 2.0 - 2.5 % | ISO 6964 | ||
| Melt Flow | 0.10 g/10 min @Load 2.16 kg | 0.10 g/10 min @Load 4.76 lb | ISO 1133 | ||
| 0.45 g/10 min @Load 5.00 kg | 0.45 g/10 min @Load 11.0 lb | ISO 1133 | |||
| High Load Melt Index | 12 g/10 min @Load 21.6 kg | 12 g/10 min @Load 47.6 lb | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 61 | 61 | DIN 53505 | ||
| Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 527 | ||
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527 | ||
| Elongation at Break | >= 700 % | >= 700 % | ISO 527 | ||
| Elongation at Yield | 9.0 % | 9.0 % | ISO 527 | ||
| Modulus of Elasticity | 1.05 GPa | 152 ksi | ISO 178 | ||
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D 790 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 93 | ||
| Dielectric Constant | 2.4 @Frequency 1000 Hz | 2.4 @Frequency 1000 Hz | IEC 250 | ||
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | IEC 243 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 175 J/g | 75.3 BTU/lb | DSC | ||
| CTE, linear | 160 μm/m-°C @Temperature 20.0 °C | 88.9 μin/in-°F @Temperature 68.0 °F | |||
| Specific Heat Capacity | 2.00 J/g-°C | 0.478 BTU/lb-°F | DSC | ||
| 2.60 J/g-°C @Temperature 150 °C | 0.621 BTU/lb-°F @Temperature 302 °F | DSC | |||
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft2-°F | DIN 52612 | ||
| 0.200 W/m-K @Temperature 150 °C | 1.39 BTU-in/hr-ft2-°F @Temperature 302 °F | DIN 52612 | |||
| Melting Point | 128 - 131 °C | 262 - 268 °F | crystalline; DSC | ||
| Vicat Softening Point | 127 °C | 261 °F | ISO 306 | ||
| Descriptive Properties | |||||
| Food Status | This material conforms to both European and American Food contact regulations. | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.