- 熔體流動速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.952
- 缺口沖擊強度: 2.14
- 拉伸強度 [MPa]: 26.2
- 彎曲模量 [MPa]: 1.31
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D 792 |
| Environmental Stress Crack Resistance | 100 hour | 100 hour | ASTM D1697 cond. B 10% lgepal |
| 600 hour | 600 hour | ASTM D1697 cond. B 100% lgepal | |
| Melt Flow | 0.25 g/10 min @Load 2.16 kg | 0.25 g/10 min @Load 4.76 lb | ASTM D 1238 |
| High Load Melt Index | 20 g/10 min @Load 21.6 kg | 20 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 26.2 MPa | >= 3800 psi | ASTM D 638 type IV |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D 638 type IV |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D 790 |
| Izod Impact, Notched | 2.14 J/cm @Thickness 3.17 mm | 4.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Tensile Load, Notched Constant | >= 24.0 hour | >= 24.0 hour | 15% yield strength; ASTM D 5397 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 128 °C | 263 °F | ASTM D3417 |