- 熔體流動速率 [g/10min]: 0.07
- 密度 [g/cm3]: 0.959
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.959 g/cc | 0.0346 lb/in3 | ASTM D 792 |
| Water Vapor Transmission | 6.20 g/m2/day | 0.399 g/100 in2/day | 100°F; E 96/66 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.070 g/10 min @Load 2.16 kg | 0.070 g/10 min @Load 4.76 lb | ISO 1133 |
| 0.35 g/10 min @Load 5.00 kg | 0.35 g/10 min @Load 11.0 lb | ISO 1133 | |
| High Load Melt Index | 9.5 g/10 min @Load 21.6 kg | 9.5 g/10 min @Load 47.6 lb | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | >= 42.7 MPa | >= 6200 psi | ASTM D 882 A |
| Film Tensile Strength at Yield, TD | >= 52.4 MPa | >= 7600 psi | ASTM D 882 A |
| Film Elongation at Break, MD | 300 - 500 % | 300 - 500 % | ASTM D 882 A |
| Film Elongation at Break, TD | 300 - 500 % | 300 - 500 % | ASTM D 882 A |
| Secant Modulus, MD | 0.910 GPa | 132 ksi | ASTM D 882 A |
| Secant Modulus, TD | 1.00 GPa | 145 ksi | ASTM D 882 A |
| Elmendorf Tear Strength MD | 22 g | 22 g | ASTM D 1922 |
| Elmendorf Tear Strength TD | 140 g | 140 g | ASTM D 1922 |
| Dart drop Test | 320 g | 0.706 lb | ASTM D 1709 |
| Film Tensile Strength at Break, MD | >= 68.9 MPa | >= 10000 psi | ASTM D 882 A |
| Film Tensile Strength at Break, TD | >= 63.8 MPa | >= 9250 psi | ASTM D 882 A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 129 °C | 265 °F | ASTM D3417 |