- 熔體流動速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.955
- 拉伸強度 [MPa]: 27.6
- 彎曲模量 [MPa]: 1.38
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in3 | ASTM D 792 |
| Environmental Stress Crack Resistance | 40 hour | 40 hour | ASTM D1693 cond. B 10% lgepal |
| 70 hour | 70 hour | ASTM D1693 cond. B 100% lgepal | |
| Melt Flow | 0.25 g/10 min @Load 2.16 kg | 0.25 g/10 min @Load 4.76 lb | ASTM D 1238 |
| High Load Melt Index | 29 g/10 min @Load 21.6 kg | 29 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 27.6 MPa | >= 4000 psi | ASTM D 638 type IV |
| Elongation at Break | 600 % | 600 % | ASTM D 638, type IV |
| Flexural Modulus | 1.38 GPa | 200 ksi | ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 129 °C | 264 °F | ASTM D3417 |