- 熔體流動速率 [g/10min]: 0.055
- 密度 [g/cm3]: 0.952
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | Exxon Method |
| Thickness | 12.7 microns | 0.500 mil | |
| Melt Flow | 0.055 g/10 min | 0.055 g/10 min | Exxon Method (I2). HLMI (I21) is 9 g/10 min. |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 34.0 MPa | 4930 psi | ASTM D882 |
| Film Elongation at Break, MD | 270 % | 270 % | ASTM D882 |
| Film Elongation at Break, TD | 430 % | 430 % | ASTM D882 |
| Secant Modulus, MD | 1.285 GPa | 186.4 ksi | ASTM D882 |
| Secant Modulus, TD | 1.415 GPa | 205.2 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.394 g/micron | 10.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 5.51 g/micron | 140 g/mil | ASTM D1922 |
| Dart Drop | 16.9 g/micron | 430 g/mil | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 95.0 MPa | 13800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 66.0 MPa | 9570 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 129 °C | 264 °F | Exxon Method |