- 熔體流動速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.935
- 拉伸強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 0.650
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in3 | ISO 1183 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | 100% ant.; ASTM D1693-70 |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg | 0.90 g/10 min @Load 4.76 lb | ISO 1133 |
| High Load Melt Index | 25 g/10 min @Load 21.6 kg | 25 g/10 min @Load 47.6 lb | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO 527 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO 527 |
| Elongation at Break | >= 700 % | >= 700 % | ISO 527 |
| Elongation at Yield | 12 % | 12 % | ISO 527 |
| Flexural Modulus | 0.650 GPa | 94.3 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | ASTM D3417 |
| Optical Properties | Metric | English | Comments |
| Gloss | 60 - 90 % | 60 - 90 % | 60 Degrees |