- 熔體流動速率 [g/10min]: 0.3
- 脆化溫度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.953 g/cc | 0.953 g/cc | ISO 1183 |
| Thickness | 10.0 - 50.0 microns | 0.394 - 1.97 mil | Recommended |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 23 g/10 min @Load 21.6 kg, Temperature 190 °C | 23 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 500 % | 500 % | ISO 527-3 |
| Film Elongation at Break, TD | 650 % | 650 % | ISO 527-3 |
| Elmendorf Tear Strength, MD | 1.019 g/micron | 25.88 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 2.5475 g/micron | 64.706 g/mil | ISO 6383-2 |
| Dart drop Test | 70.0 g | 0.154 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 45.0 MPa | 6530 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 650 MPa | 94300 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 800 MPa | 116000 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 135 °C | 275 °F | Internal method |
| Vicat Softening Point | 127 °C @Load 1.00 kg | 261 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |