- 熔體流動速率 [g/10min]: 9.0
- 密度 [g/cm3]: 0.956
- 拉伸強度 [MPa]: 22.3
- 彎曲模量 [MPa]: 0.958
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.956 g/cc | 0.0345 lb/in3 | ASTM D792 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 9.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| Tensile Strength, Yield | 22.3 MPa | 3240 psi | ASTM D638 |
| Elongation at Break | 650 % | 650 % | ASTM D638 |
| Flexural Modulus | 0.958 GPa | 139 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 128 °C | 262 °F | Rate A, Loading 1 (10 N); ASTM D1525 |