- 熔體流動速率 [g/10min]: 0.2
- 缺口沖擊強度: 1.8
- 拉伸強度 [MPa]: 27.0
- 彎曲模量 [MPa]: 1.20
- 脆化溫度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.953 g/cc | 0.953 g/cc | ISO 1183 |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | ISO 22088 |
| Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.20 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 0.80 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.80 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |
| 21 g/10 min @Load 21.6 kg, Temperature 190 °C | 21 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64 | 64 | ISO 868/A |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ISO 527 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ISO 527 |
| Elongation at Break | >= 600 % | >= 600 % | ISO 527 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ISO 178 |
| Izod Impact, Notched | 1.80 J/cm | 3.37 ft-lb/in | ISO 180/A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 135 °C | 275 °F | Internal method |
| Vicat Softening Point | 125 °C @Load 1.00 kg | 257 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |