- 熔體流動速率 [g/10min]: 10.0
- 密度 [g/cm3]: 0.964
- 拉伸強度 [MPa]: 27.0
- 彎曲模量 [MPa]: 1.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.964 g/cc | 0.0348 lb/in3 | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 190 °C | 10 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 68 | 68 | ASTM D2240 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 131 °C | 268 °F | Rate A, Loading 1 (10 N); ASTM D1525 |