- 熔體流動速率 [g/10min]: 12.5
- 密度 [g/cm3]: 0.95
- 缺口沖擊強度: 2.2
- 拉伸強度 [MPa]: 25.0
- 彎曲強度 [MPa]: 33.0
- 彎曲模量 [MPa]: 1.05
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in3 | ASTM D792 |
| Environmental Stress Crack Resistance | >= 1500 hour | >= 1500 hour | F50, Condition A, ASTM D1693, 100% Igepal |
| Melt Flow | 12.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 12.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength, Ultimate | 33.0 MPa | 4790 psi | ASTM D638 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| Elongation at Break | 800 % | 800 % | ASTM D638 |
| Tensile Modulus | 0.990 GPa | 144 ksi | Secant; ASTM D638 |
| Flexural Modulus | 1.05 GPa | 152 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 2.20 J/cm | 4.12 ft-lb/in | Notched/Unnotched not specified; ASTM D256 |
| Tensile Impact Strength | 325 kJ/m2 | 155 ft-lb/in2 | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 131 °C | 268 °F | ASTM D3417 |
| Vicat Softening Point | 121 °C | 250 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 220 °C | 410 - 428 °F | |