- 熔體流動速率 [g/10min]: 10.0
- 密度 [g/cm3]: 0.952
- 缺口沖擊強度: 3.9
- 拉伸強度 [MPa]: 25.0
- 彎曲模量 [MPa]: 1.28
- 脆化溫度 [℃]: -100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D792 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50, Condition B, ASTM D1693, 100% Igepal AND Condition A, 20% Igepal |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 190 °C | 10 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| Elongation at Break | 820 % | 820 % | ASTM D638 |
| Flexural Modulus | 1.28 GPa | 186 ksi | ASTM D790 |
| Izod Impact, Notched | 3.90 J/cm | 7.31 ft-lb/in | Notched/Unnotched not specified; ASTM D256 |
| Tensile Impact Strength | 320 kJ/m2 | 152 ft-lb/in2 | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D696 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |