- 熔體流動速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.949
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in3 | ASTM D792 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.40 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 22.0 MPa | 3190 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 24.0 MPa | 3480 psi | ASTM D882 |
| Film Elongation at Break, MD | 529 % | 529 % | ASTM D882 |
| Film Elongation at Break, TD | 892 % | 892 % | ASTM D882 |
| Secant Modulus, MD | 0.638 GPa | 92.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.769 GPa | 112 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.500 g/micron | 12.7 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 18.7 g/micron | 475 g/mil | ASTM D1922 |
| Dart Drop | 2.70 g/micron | 68.6 g/mil | F50, ASTM D1709/A |
| Film Tensile Strength at Break, MD | 35.0 MPa | 5080 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 33.0 MPa | 4790 psi | ASTM D882 |