- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.945
- 彎曲模量 [MPa]: 0.862
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 - 0.965 g/cc | 0.0341 - 0.0349 lb/in3 | ASTM D1505 |
| Melt Flow | 6.0 - 27 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 - 27 g/10 min @Load 4.76 lb, Temperature 374 °F | Procedure A Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 19.3 - 27.6 MPa | 2800 - 4000 psi | ASTM D638 |
| Elongation at Break | 5.0 - 400 % | 5.0 - 400 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 0.862 - 1.21 GPa | 125 - 175 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |