- 熔體流動速率 [g/10min]: 0.1
- 密度 [g/cm3]: 1.11
- 拉伸強度 [MPa]: 32.6
- 彎曲模量 [MPa]: 1.516
- 熱變形溫度 [℃]: 89.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in3 | ASTM D1505 |
| Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 29.8 g/10 min @Load 21.6 kg, Temperature 190 °C | 29.8 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 32.6 MPa | 4730 psi | ASTM D638 |
| Elongation at Break | >= 110 % | >= 110 % | ASTM D638 |
| Flexural Strength | 29.3 MPa | 4250 psi | ASTM D790 |
| Flexural Modulus | 1.516 GPa | 219.9 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 89.6 °C | 193 °F | 0.125";; ASTM D648 |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |