- 熔體流動速率 [g/10min]: 4.9
- 密度 [g/cm3]: 0.942
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in3 | ASTM-D792 | ||
| Melt Flow | 4.9 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.9 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 1350 % | 1350 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 430 % | 430 % | ASTM-D882 | ||
| Elmendorf Tear Strength MD | 13 g | 13 g | ASTM-D1922 | ||
| Elmendorf Tear Strength TD | 20 g | 20 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, MD | 0.520 g/micron | 13.2 g/mil | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 0.800 g/micron | 20.3 g/mil | ASTM-D1922 | ||
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM-D882 | ||
| 1% Secant Modulus, MD | 490 MPa | 71100 psi | ASTM-D882 | ||
| 1% Secant Modulus, TD | 540 MPa | 78300 psi | ASTM-D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 66 % | 66 % | ASTM-D1003 | ||
| Gloss | 16 % | 16 % | Angle 60°; ASTM-D2457 | ||
| Descriptive Properties | |||||
| Temperature Profile (°C) | 180-250 | Extrusion | |||
| 250-290 | Die Head and Die | ||||