- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.25
- 缺口沖擊強度: 0.641
- 拉伸強度 [MPa]: 47.0
- 彎曲模量 [MPa]: 4.300
- 硬度: 52.0
- 熱變形溫度 [℃]: 129.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | MD; ASTM D955 |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 52 | 52 | ASTM D785 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 4.400 GPa | 638.1 ksi | ASTM D638 |
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Flexural Modulus | 4.300 GPa | 623.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 264 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | |