- 熔體流動速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.96
- 拉伸強度 [MPa]: 31.0
- 彎曲模量 [MPa]: 1.55
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in3 | ASTM D1505 | ||
| ESCR 100% Igepal? | 10 hour | 10 hour | |||
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 2 in/min (50 mm/min); ASTM D638 | ||
| Elongation at Break | >= 300 % | >= 300 % | 2 in/min (50 mm/min); ASTM D638 | ||
| Flexural Modulus | 1.55 GPa | 225 ksi | Tangent Method 1; ASTM D-790 | ||
| Descriptive Properties | |||||
| process | Blow Molding | ||||
| region | Europe/Turkey | ||||