- 熔體流動速率 [g/10min]: 0.05
- 密度 [g/cm3]: 0.952
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D1505 | ||
| Thickness | 20.0 microns | 0.787 mil | 4:1 blow-up ratio | ||
| Melt Flow | 0.050 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.050 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D-1238 | ||
| High Load Melt Index | 6.5 g/10 min @Load 21.6 kg, Temperature 190 °C | 6.5 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 200 % | 200 % | >200; ASTM D-882, A | ||
| Film Elongation at Break, TD | 200 % | 200 % | >200; ASTM D-882, A | ||
| Elmendorf Tear Strength, MD | 1.08 g/micron | 27.4 g/mil | ASTM D-1922 | ||
| Elmendorf Tear Strength, TD | 6.20 g/micron | 157 g/mil | ASTM D-1922 | ||
| Dart Drop | 12.8 g/micron | 325 g/mil | ASTM D-1709 | ||
| Film Tensile Strength at Break, MD | 52.0 MPa | 7540 psi | |||
| Film Tensile Strength at Break, TD | 33.0 MPa | 4790 psi | |||
| Descriptive Properties | |||||
| process | Blown Film | ||||
| region | Europe/Turkey | ||||