- 熔體流動(dòng)速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.954
- 缺口沖擊強(qiáng)度: 0.43
- 拉伸強(qiáng)度 [MPa]: 24.8
- 彎曲模量 [MPa]: 1.31
- 熱變形溫度 [℃]: 80.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in3 | ASTM D1505 | ||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | 2 in/min (50 mm/min); ASTM D638 | ||
| Elongation at Break | 350 % | 350 % | 2 in/min (50 mm/min); ASTM D638 | ||
| Flexural Modulus | 1.31 GPa | 190 ksi | Tangent Method 1; ASTM D-790 | ||
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 | ||
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| process | Injection Molding | ||||