- 熔體流動速率 [g/10min]: 0.265
- 密度 [g/cm3]: 0.94
- 缺口沖擊強度: 3.2
- 拉伸強度 [MPa]: 17.5
- 彎曲強度 [MPa]: 22.0
- 彎曲模量 [MPa]: 0.580
- 脆化溫度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 - 0.956 g/cc | 0.0340 - 0.0345 lb/in3 | Average value: 0.950 g/cc Grade Count:8 |
| Environmental Stress Crack Resistance | 400 - 5000 hour | 400 - 5000 hour | Average value: 3170 hour Grade Count:6 |
| Melt Flow | 0.265 - 34.0 g/10 min | 0.265 - 34.0 g/10 min | Average value: 9.32 g/10 min Grade Count:10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59.0 - 68.0 | 59.0 - 68.0 | Average value: 64.3 Grade Count:7 |
| Tensile Strength, Ultimate | 22.0 - 31.0 MPa | 3190 - 4500 psi | Average value: 28.3 MPa Grade Count:6 |
| Tensile Strength, Yield | 17.5 - 23.4 MPa | 2540 - 3390 psi | Average value: 21.2 MPa Grade Count:7 |
| Elongation at Break | 600 - 800 % | 600 - 800 % | Average value: 771 % Grade Count:7 |
| Flexural Modulus | 0.580 - 0.830 GPa | 84.1 - 120 ksi | Average value: 0.760 GPa Grade Count:6 |
| Izod Impact, Notched | 3.20 - 7.50 J/cm | 5.99 - 14.1 ft-lb/in | Average value: 4.64 J/cm Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 115 - 129 °C | 239 - 264 °F | Average value: 124 °C Grade Count:6 |
| Brittleness Temperature | -118 - -70.0 °C | -180 - -94.0 °F | Average value: -86.6 °C Grade Count:7 |