- 熔體流動速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.924
- 拉伸強度 [MPa]: 10.3
- 彎曲模量 [MPa]: 0.310
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | ASTM D792 | ||
| Thickness | >= 25.0 microns | >= 0.984 mil | |||
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.2 MPa | 1620 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ASTM D882 | ||
| Tensile Strength, Yield | 10.3 MPa | 1490 psi | ASTM D638 | ||
| Film Elongation at Break, MD | 186 % | 186 % | ASTM D882 | ||
| Film Elongation at Break, TD | 513 % | 513 % | ASTM D882 | ||
| Elongation at Break | 600 % | 600 % | ASTM D638 | ||
| Flexural Modulus | 0.310 GPa | 45.0 ksi | at 1%; ASTM D790 | ||
| Secant Modulus, MD | 0.193 GPa | 28.0 ksi | at 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.513 GPa | 74.4 ksi | at 1%; ASTM D882 | ||
| Impact | 43.2 | 43.2 | J/mm; NOVA Chemicals Puncture test | ||
| Coefficient of Friction | >= 0.60 | >= 0.60 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 10.5 g/micron | 267 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 3.90 g/micron | 99.1 g/mil | ASTM D1922 | ||
| Dart Drop | 2.40 g/micron | 61.0 g/mil | F50, ASTM D1709/A | ||
| Film Tensile Strength at Break, MD | 27.2 MPa | 3950 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 17.8 MPa | 2580 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 9.9 % | 9.9 % | ASTM D1003 | ||
| Gloss | 49.3 % | 49.3 % | at 45°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 170 - 190 °C | 338 - 374 °F | |||
| Descriptive Properties | |||||
| Blow Up Ratio | 2:1 to 3:1 | ||||