- 熔體流動速率 [g/10min]: 1.9
- 彎曲模量 [MPa]: 1.79
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.920 g/cc | 0.920 g/cc | ASTM D792 |
| Melt Flow | 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.9 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 14.5 MPa | 2100 psi | ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 |
| Flexural Modulus | 1.79 GPa | 260 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 95.6 °C | 204 °F | ASTM D648 |