- 熔體流動速率 [g/10min]: 3.1
- 彎曲強度 [MPa]: 12.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.918 - 0.921 g/cc | 0.918 - 0.921 g/cc | ASTM D1505 |
| Melt Flow | 3.1 - 3.5 g/10 min @Load 2.61 kg, Temperature 190 °C | 3.1 - 3.5 g/10 min @Load 5.75 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 12.3 MPa | 1780 psi | 500mm/min; ASTM D638 |
| Elongation at Break | 600 % | 600 % | 500 mm/min, Ultimate; ASTM D638 |
| 2% Secant Modulus | 1.10 GPa | 160 ksi | 500mm/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 105 °C | 221 °F | 10°C/min; ASTM D3418 |