- 熔體流動速率 [g/10min]: 1.9
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | ISO 1183 | ||
| Melt Flow | 1.9 g/10 min | 1.9 g/10 min | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 11.0 MPa | 1600 psi | at Yield, TD; ISO R527-1 | ||
| 13.0 MPa | 1890 psi | at Yield, MD; ISO R527-1 | |||
| Film Elongation at Break, MD | >= 150 % | >= 150 % | ISO R527-1 | ||
| Film Elongation at Break, TD | >= 500 % | >= 500 % | ISO R527-1 | ||
| Modulus of Elasticity | 0.190 GPa | 27.6 ksi | MD; ISO R527-1 | ||
| 0.200 GPa | 29.0 ksi | TD; ISO R527-1 | |||
| Tensile Impact | 260 J/cm | 487 ft-lb/in | ASTM D4272 | ||
| Coefficient of Friction | 1.0 | 1.0 | ASTM D1894 | ||
| Tear Strength | 25.0 kN/m | 143 pli | TD; ISO 6383-2 | ||
| 60.0 kN/m | 342 pli | MD; ISO 6383-2 | |||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ISO R527-1 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 11 % | 11 % | ASTM D1003A | ||
| Gloss | 50 % | 50 % | ASTM D2457 | ||
| Descriptive Properties | |||||
| Clarity, mV | 29 | Sabtec | |||