- 熔體流動速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | ISO 1183 | ||
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 11.0 MPa | 1600 psi | at Yield, TD; ISO R527-1 | ||
| 12.0 MPa | 1740 psi | at Yield, MD; ISO R527-1 | |||
| Film Elongation at Break, MD | >= 200 % | >= 200 % | ISO R527-1 | ||
| Film Elongation at Break, TD | >= 500 % | >= 500 % | ISO R527-1 | ||
| Modulus of Elasticity | 0.160 GPa | 23.2 ksi | MD; ISO R527-1 | ||
| 0.170 GPa | 24.7 ksi | TD; ISO R527-1 | |||
| Tensile Impact | 300 J/cm | 562 ft-lb/in | ASTM D4272 | ||
| Coefficient of Friction | 0.10 | 0.10 | ASTM D1894 | ||
| Tear Strength | 30.0 kN/m | 171 pli | TD; ISO 6383-2 | ||
| 40.0 kN/m | 228 pli | MD; ISO 6383-2 | |||
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO R527-1 | ||
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ISO R527-1 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 11 % | 11 % | ASTM D1003A | ||
| Gloss | 49 % | 49 % | ASTM D2457 | ||
| Descriptive Properties | |||||
| Clarity, mV | 37 | Sabtec | |||