- 熔體流動速率 [g/10min]: 6.5
- 密度 [g/cm3]: 0.922
- 拉伸強度 [MPa]: 11.0
- 彎曲強度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in3 | ASTM D1505 |
| Melt Flow | 6.5 g/10 min | 6.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 48 | 48 | ASTM D2240 |
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Film Elongation at Break, MD | 320 % | 320 % | ASTM D882 |
| Film Elongation at Break, TD | 380 % | 380 % | ASTM D882 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Modulus of Elasticity | 0.297 GPa | 43.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.204 GPa | 29.6 ksi | ASTM D882 |
| Secant Modulus, TD | 0.255 GPa | 37.0 ksi | ASTM D882 |
| Dart drop Test | 50.0 g | 0.110 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 14.0 MPa | 2030 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 16.0 MPa | 2320 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Gloss | 49 % | 49 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 150 - 160 °C | 302 - 320 °F | |