- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.922
- 拉伸強度 [MPa]: 10.0
- 彎曲強度 [MPa]: 15.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in3 | ASTM D1505 |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 44 | 44 | ASTM D2240 |
| Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Film Elongation at Break, MD | 168 % | 168 % | ASTM D882 |
| Film Elongation at Break, TD | 249 % | 249 % | ASTM D882 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Modulus of Elasticity | 0.276 GPa | 40.0 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.186 GPa | 27.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.235 GPa | 34.1 ksi | ASTM D882 |
| Dart drop Test | 93.0 g | 0.205 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 18.0 MPa | 2610 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 93.0 °C | 199 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 20 % | 20 % | ASTM D1003 |
| Gloss | 35 % | 35 % | at 45°; ASTM D523 |