- 熔體流動速率 [g/10min]: 60.0
- 密度 [g/cm3]: 0.924
- 拉伸強(qiáng)度 [MPa]: 12.0
- 彎曲強(qiáng)度 [MPa]: 9.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | ASTM D1505 |
| Melt Flow | 60 g/10 min | 60 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength, Ultimate | 9.00 MPa | 1310 psi | ASTM D638 |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Modulus of Elasticity | 0.345 GPa | 50.0 ksi | Secant; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 98.0 °C | 208 °F | ASTM D1525 |