- 熔體流動(dòng)速率 [g/10min]: 9.0
- 密度 [g/cm3]: 0.917
- 拉伸強(qiáng)度 [MPa]: 9.0
- 彎曲強(qiáng)度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in3 | ASTM D1505 |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 44 | 44 | ASTM D2240 |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM D638 |
| Elongation at Break | 475 % | 475 % | ASTM D638 |
| Modulus of Elasticity | 0.169 GPa | 24.5 ksi | Secant; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 85.0 °C | 185 °F | ASTM D1525 |