- 熔體流動速率 [g/10min]: 7.5
- 拉伸強度 [MPa]: 5.0
- 彎曲模量 [MPa]: 0.0600
- 脆化溫度 [℃]: -70.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ISO 1183 |
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 7.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 28 | 28 | ISO 868/A |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO 527 |
| Tensile Strength, Yield | 5.00 MPa | 725 psi | ISO 527 |
| Elongation at Break | 750 % | 750 % | ISO 527 |
| Flexural Modulus | 0.0600 GPa | 8.70 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 113 °C | 235 °F | Internal method |
| Vicat Softening Point | 60.0 °C @Load 1.00 kg | 140 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |