- 熔體流動速率 [g/10min]: 4.7
- 密度 [g/cm3]: 0.9225
- 彎曲模量 [MPa]: 0.276
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9225 g/cc | 0.03333 lb/in3 | ASTM D1505 |
| Particle Size | 5.0 - 50 μm | 5.0 - 50 μm | Spherical shape, 5-50 micron distribution. ETM = Equistar Test Method; ETM Malvern |
| Maximum Moisture Content | 0.10 | 0.10 | ETM 156 |
| Melt Flow | 4.7 g/10 min | 4.7 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 53 | 53 | ASTM D2240 |
| Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D638 |
| Elongation at Break | 550 % | 550 % | ASTM D638 |
| Flexural Modulus | 0.276 GPa | 40.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | ASTM D3418 |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D1525 |
| Brittleness Temperature | -76.0 °C | -105 °F | ASTM D746 |