- 熔體流動速率 [g/10min]: 3.5
- 拉伸強度 [MPa]: 10.0
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.920 g/cc | 0.920 g/cc | ISO 1183 |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 44 | 44 | ISO 868/A |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ISO 527 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ISO 527 |
| Elongation at Break | 520 % | 520 % | ISO 527 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 111 °C | 232 °F | Internal method |
| Vicat Softening Point | 89.0 °C @Load 1.00 kg | 192 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |