- 熔體流動速率 [g/10min]: 0.77
- 密度 [g/cm3]: 0.911
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.911 g/cc | 0.0329 lb/in3 | ASTM D792 |
| Melt Flow | 0.77 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.77 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 7.00 MPa | 1020 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.00 MPa | 1020 psi | ASTM D882 |
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Break, TD | 1000 % | 1000 % | ASTM D882 |
| Secant Modulus, MD | 0.145 GPa | 21.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.135 GPa | 19.6 ksi | ASTM D882 |
| Coefficient of Friction | >= 1.0 | >= 1.0 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 16.0 g/micron | 406 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 21.0 g/micron | 533 g/mil | ASTM D1922 |
| Dart Drop | 28.0 g/micron | 711 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 46.0 MPa | 6670 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % @Thickness 0.0250 mm | 7.0 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 60 % | 60 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 215 - 225 °C | 419 - 437 °F | |