- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | ASTM D4883 | ||
| Thickness | 76.0 microns | 2.99 mil | |||
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 25.0 MPa | 3630 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 320 % | 320 % | ASTM D882 | ||
| Film Elongation at Break, TD | 885 % | 885 % | ASTM D882 | ||
| Secant Modulus, MD | 0.193 GPa | 28.0 ksi | 1% Secant; ASTM D882 | ||
| Secant Modulus, TD | 0.231 GPa | 33.5 ksi | 1% Secant; ASTM D882 | ||
| Elmendorf Tear Strength MD | 355 g | 355 g | |||
| Elmendorf Tear Strength TD | 334 g | 334 g | |||
| Elmendorf Tear Strength, MD | 4.66 g/micron | 118 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 4.33 g/micron | 110 g/mil | ASTM D1922 | ||
| Dart Drop | 4.19 g/micron | 106 g/mil | ASTM D1709A | ||
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 12 % | 12 % | ASTM D1003 | ||
| Gloss | 53 % | 53 % | at 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Process | Film | ||||
| region | US & Canada | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.