- 熔體流動速率 [g/10min]: 0.22
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | |
| Thickness | 76.0 microns | 2.99 mil | |
| Melt Flow | 0.22 g/10 min @Load 2.16 kg | 0.22 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.3 MPa | 1490 psi | |
| Film Tensile Strength at Yield, TD | 9.70 MPa | 1410 psi | |
| Film Elongation at Break, MD | 450 % | 450 % | |
| Film Elongation at Break, TD | 540 % | 540 % | |
| Coefficient of Friction | 0.70 | 0.70 | |
| Elmendorf Tear Strength MD | 290 g | 290 g | |
| Elmendorf Tear Strength TD | 380 g | 380 g | |
| Elmendorf Tear Strength, MD | 3.80 g/micron | 96.5 g/mil | |
| Elmendorf Tear Strength, TD | 5.00 g/micron | 127 g/mil | |
| Dart Drop | 3.90 g/micron | 99.1 g/mil | |
| Film Tensile Strength at Break, MD | 23.4 MPa | 3390 psi | |
| Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | |
| Optical Properties | Metric | English | Comments |
| Haze | 12 % | 12 % | |
| Gloss | 52 % | 52 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 216 °C | 421 °F | Film extrusion temperature |